基于博弈论集对分析的硫化矿石自燃倾向预测方法研究
张 悦,刘 杰,傅 钰,邓禾苗,金 龙
((昆明理工大学 公共安全与应急管理学院,昆明 650093))
Research on prediction of spontaneous combustion tendency of sulfide ores based on game theory and set pair analysis
ZHANG Yue, LIU Jie, FU Yu, DENG Hemiao, JIN Long
((School of Public Safety and Emergency Management, Kunming University of Science and Technology, Kunming 650093, China))
摘要
图/表
参考文献
相似文献
本文已被:浏览 169次   下载 160
投稿时间:2020-10-14    修订日期:2020-11-03
中文摘要: 文章基于博弈论和集对分析方法,选取判矿样的低温氧化质量增加率、自热点和着火点,为基本判定因子,利用层次分析法和熵权法得到主客观权重,通过博弈论组合赋权得出最优组合权重;根据集对分析法算出相应的指标联系度,结合各个指标的权重计算出综合联系度,最终确定各矿样的自燃倾向性等级。通过10组国内典型矿山样本数据,运用该分析方法得出的结论与实际结果基本相符
Abstract:Based on game theory and set pair analysis method, this paper select the increase rate of low temperature oxidation mass, self-hot spot and ignition point of ore samples as the basic judgment factors, and obtained the subjective and objective weight by analytic hierarchy process and entropy weight method, and obtained the optimal combination weight by the combination weight of game theory. According to the set pair analysis method, the corresponding index correlation degree was calculated, and the comprehensive correlation degree was calculated based on the weight of each index. Finally, the spontaneous combustion tendency grade of each mineral sample was determined. Based on 10 sets of data from typical mines in China, the conclusions obtained by using this analysis method were basically consistent with the actual results.
文章编号:     中图分类号:X913    文献标志码:
基金项目:云南省科技厅重点研发计划(202003AC100002)
引用文本:
张 悦,刘 杰,傅 钰,邓禾苗,金 龙.基于博弈论集对分析的硫化矿石自燃倾向预测方法研究[J].有色金属(矿山部分),2021,73(3):141-146.
ZHANG Yue,LIU Jie,FU Yu,DENG Hemiao,JIN Long.Research on prediction of spontaneous combustion tendency of sulfide ores based on game theory and set pair analysis[J].NONFERROUS METALS(Mining Section),2021,73(3):141-146.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299757

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299757

传真:010-63299754

QQ:XXXXXXX

Email:ysks@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号