中文摘要: 对云南金满铜矿的灰色和紫色两种板岩进行单轴压缩试验。试验结果表明:两种板岩都具有明显的各向异性。灰色板岩在平行层理加载下的抗压强度、平均弹性模量和平均泊松比与垂直层理加载的比值分别为:0.62,1.66,8.68;紫色板岩的比值为1.63,8.38,34.64。当体积应变ε<0和泊松比μ>0.5时就能反映出岩石在加载过程中产生了扩容现象。在平行层理加载下的体积应变在较低的应力(破坏载荷的5 %~20 %)处就产生了明显的扩容,而在垂直层理加载下的体积应变临近破坏时才出现扩容现象。
Abstract:Uniaxial compressive tests were carried out with two types of slate samples from Jinman copper mine, Yunnan. Experiment results demonstrated that both rocks have obvious anisotropy. Values of compressive strength, average elastic modulus and the average Poisson’s ratio of the grey slate subjected to loading parallel to bedding stratum corresponding to values subjected to loading perpendicular to bedding were 0.62, 1.66 and 8.68 respectively. Which of them in purple slate were 1.63, 8.38 and 34.64. Dilation phenomenon of the slate appears during the loading process, when volume strain was less than 0 or Poisson"s ratio is larger than 0.5. Dilation appears significantly at lower stress in slate subjected to loading parallel to bedding, while dilation occurs at stress near to failure in slate subjected to loading perpendicular to bedding.
文章编号:     中图分类号:    文献标志码:
基金项目:
引用文本:
陈超.板岩各向异性试验研究[J].有色金属(矿山部分),2011,63(3):0.
CHEN Chao.Experimental study on the anisotropy of schist samples[J].NONFERROUS METALS(Mining Section),2011,63(3):0.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299757

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299757

传真:010-63299754

QQ:XXXXXXX

Email:ysjsks@sina.com;ysjsks@163.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号